Do non-pressure / non-hydrocarbon containing parts (316L SS) on Gas Turbines need to be painted? There would be no significant consequences if chloride stress corrosion cracking occurs.
Confirm to permanently remove your answer!
It is not the rule or requirement from any class society, but many operators in the offshore environment prefer to paint the following items even though they are non-pressure / non-hydrocarbon containing parts.
Detailed corrosion prediction evaluations including consideration for CO2 should be performed to establish a materials selection and corrosion control report …
Prevention of Chloride stress corrosion cracking [CSCC] in austenitic stainless steel material for closed loop water/glycol mixture are as follows:Elimination …
Chloride Stress Corrosion CrackingFor Chloride Stress Corrosion Cracking (SCC) to occur, one of the following criteria has to take place:Chloride …
The hot section of the gas turbine can get damaged by the presence of hydrocarbon liquid in the fuel gas. …
The following are considerations associated with steam systems that have special significance for the steam trap user and designer alike. …